Description
Performance summary
DC -758C shoe thick paste mainly applied to the transparent plate mesh . Space leather . Upper high-elastic material, and nylon thick version of printing; characterized by ease of use, high bulk, soft feel, good flexibility, resistance to cold bending off ( -2 0 deg.] C – -3 0 deg.] C or more bending 80,000 times) , good adhesion, good acid and alkali resistance, UV resistant, non-yellowing. The product meets environmental protection standards, has excellent frost resistance, does not contain formaldehyde, and does not contain APEO .
Product properties
Appearance: milky white paste
Composition: polyurethane and additives
P H ：7.5~8.5
Reference prescription
| Base printing | Color printing | ||||||||||||||||||||||||||||
|
|
Printing process
Self-drying ( 96 hours)
Printing and drying ( 6-8 times for printing on the bottom , 2-4 times for coloring )
Baking ( 80 ℃× 8 hours and minutes)
Precautions
1. Since DC-758C is used with a special cross-linking agent, customers are not allowed to change or increase or decrease the cross-linking agent at will.
2, in general, must be added a cross-linking agent in the printing paste 4-8 run out within hours, otherwise the consequences and therefore , the company is not responsible.
3. Due to the special requirements of shoe upper printing, the printing ink layer must be fully cross-linked before testing. Baking can shorten the cross-linking time, but it may cause the decline of product performance, so try to take natural drying to make it completely Cross-linking takes about 4 to 7 days.
4, the storage of the product is . 6 months, save in . 5 – . 3 . 5 deg.] C under dry conditions, after use the cover must be tightly closed to prevent surface crust, affecting again. Cover the bottle cap after using the matching curing agent, and do not open it in the air!
5. Different substrates and differences in processing methods may lead to a decrease in adhesion. If conditions permit, please try to eliminate static electricity generated by the substrate.
Due to the variability of chemical products, whether the company provides small samples or bulk goods, the factory needs to make samples carefully according to the specified process conditions, and can be put into mass production after the various fastness tests are qualified. The company will not bear any loss caused by untested.