Description
HR-18 low temperature high foaming pulp
Performance summary
HR-18 low temperature and high foaming pulp is suitable for printing on cotton, linen, T/C, chemical fiber and other fabrics. Its characteristics are easy to use, good printing operability, high cost performance, low foaming temperature, giving the printing surface a unique three-dimensional effect . The product complies with environmental protection standards, does not contain formaldehyde, APEO , plasticizer, heavy metals, etc., and can be used for children’s clothing printing.
Product properties
Appearance: white paste
Composition: Acrylate polymer, additives
The PH :. 7 .5 ~ 8.5
Reference prescription
|
|
White printing plus color printing |
|
HR-18 |
20-30% 20-30% |
|
1890 |
70-80% — |
|
1890A |
— 70-80% |
|
Color |
— 0-5% |
|
L-300 curing agent |
0-1% 0-1% |
|
total |
100% 100% |
Printing process
100-120 mesh screen water-based sharp knife — printing 2 knives X 3 times —drying— baking ( 120 ～ 130 ℃× 1 ～ 2 minutes)
Precautions
1. Adding curing agent L-300 1% can effectively improve the firmness of the printed surface to meet special fabrics or high-demand printing. The printing paste with curing agent must be used up within 24 hours; for high-elastic stretch fabrics The printing can be printed 1-2 times with the base transparent pulp DC-1 to improve the flexibility of printing.
2. The storage period of this product is 12 months. Please keep it in a low-temperature and dry place. The lid must be tightly closed after use to avoid skin formation on the surface, which may affect reuse.
3. Due to the variability of chemical products, whether the company provides small samples or bulk goods, the factory needs to make samples carefully according to the specified process conditions, and can be put into mass production after the various fastness tests are qualified. The company will not bear any loss caused by untested.